| Product | Components | (pbw) |
(°C) |
Pot-life | Viscosity |
Description |
|---|---|---|---|---|---|---|
|
|
A/B | 0,3-4 h/25°C | 200-400 | Combination of one resin with five hardeners, low viscosity, fast to slow reactivity. Optimal for infusion. | ||
|
|
A/B | 100/28 (34) | 90-115 (65) | 0,3-4 h/25°C | 350-650 | Combination of one resin with five hardeners, medium viscosity, fast to slow reactivity. Optimal for hand lay-up. |
|
|
A/B | 100/32 | 80-85 | 1-2 h/25°C | 200-250 | Combination of one resin with two hardeners, low viscosity, fast to slow reactivity. Optimal for wind mill blades. |
|
|
A/B | 100/37 | 130-150 | 2-3 h/25°C | 350-550 | Slow reactivity, low viscosity, high mechanical properties. |
|
|
A/B | 100/25 | 120-130 | 0,5-1 h/25°C | 300-450 | Medium reactivity, low viscosity, high mechanical properties. |
|
|
A/B | 100/40 | 115-130 | 2-3 h/25°C | 200-500 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. |
|
|
A/B | 100/32 | 80-90 | 200-500 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. | |
|
|
A/B | 100/40 | 115-130 | 0,5-1 h/25°C | 500-800 | Slow reactivity, high mechanical properties. Optimal for hand lay-up. |
|
|
A/B | 100/32 | 85-100 | 20-40 min/25°C | 300-500 | Medium reactivity, high mechanical properties. Optimal for hand lay-up. |
|
|
A/B/C1/D1 | 100/85/0.5/10 | 85-95 | > 10 h/25°C | High mechanical properties, long pot life. Curing at higher temperature (at least 80°C). | |
|
|
A/B/C2 | 100/90/1 | 130-145 | > 10 h/25°C | 500-1 000 | Long pot life, low viscosity. Curing at higher temperature (at least 80°C). |
|
|
A/B/C2 | 100/85/1 | 115-130 | > 10 h/25°C | 500-1 000 | Low viscosity. Curing at higher temperature (at least 80°C). |
|
|
A/B/C3 | 100/95/1 | 165-175 | > 10 h/25°C | 1 000-1 200 | High thermal resistance. Post curing above 160°C. |
|
|
A/B | 100/50 | 70-80 | 12-15 min/25°C | Laminated system with medium viscosity. High adhesion to dural, steel and other metal surfaces. |